May, 2012
100 SERIES SUPER GLOSS INK
INTRODUCTIONS
100 SERIES SUPER GLOSS INK forms glossy and tough ink film that has excellent physical properties such as alcohol resistance.
APPLICATIONS
Acryl plate, ABS(primed/unprimed), rigid vinyl, vinyl stickers, glossy paper, coated paper.
CHARACTERISTICS
- Good printability. Ink film is glossy with good levelling.
- Excellent adhesion
- Weathering resistance is rather good.
- Excellent resistance to oil, alcohol, gasoline and chemicals.
- Suitable for vacuum-forming.
- Dried ink film is tough and resistant to scratch.
HOW TO USE
Dilute the ink with VAC THINNER (fast drying, standard drying, slow drying). VAC RETARDER is recommended to make the drying slower.
DRYING
- Substrate : Acryl plate. Tack free : Approx.15 min.(20°C)(68°F), Approx.3 min.(60°C)(140°F)
- Complete drying : Approx.90 min.(20°C)(68°F), Approx.5 min.(60°C)(140°F)
STENCIL & WASHING UP
Use photo-stencil. Use VINYL CLEANING THINNER.
LIGHTFASTNESS
5-8 grades (Please refer to lightfastness chart)
COLOR RANGE
Standard 22 colors, EXO(extra opaque) 5 colors, matting agent.
PRECAUTIONS
- 100 SERIES SUPER GLOSS INK forms tough ink film. If plural hits are done on vinyl stickers, the substrate may curl up. Use 3500 SERIES EXG INK which is more flexible than 100 SERIES.
- 100 SERIES SUPER GLOSS INK is not suitable for styrol, AS and noryl. Good adhesion cannot be obtained.
- Although weathering resistance of SUPER GLOSS INK is rather good, 3500 SERIES EXG INK is recommended when long-life weathering resistance is required. Weathering resistance can be made even better by using JELCON SERIES VS INK(UV cutting clear ink) together with 3500 SERIES.
- Please refer to MSDS before use.
- Be sure to do trial print before commercial run to confirm that the product fits the purposes.
PHYSICAL PROPERTIES
Substrate : 3 hits on acryl plate
Printing sequence : 101 white + 190 black + 101 white
Ink is diluted with VAC THINNER (standard drying). Tetron screen 270 meshes/inch.
Drying : over 24 hours at room temperature.
| TEST ITEMS | TEST METHODS | RESULTS |
|---|---|---|
| Adhesion | Cross hatch, peeling test | 100/100 Passed |
| Impact resistance | JIS K5400 8.3.2 Du Pont Impact test 1/2 inch, 500 grams, 50cm |
No peeling off No cracks |
| Hardness | JIS K5400 8.4 scratch by pencil | 2H |
| Heat resistance | JIS K5400 8.13 80°C(176°F) 24hrs | Passed |
| Coldness resistance | -40°C(-40°F) 24hrs | Passed |
| Water-proofness | JIS K5400 8.19 Immersion in water : 80°C(176°F) 24hrs |
Passed |
| Humidity resistance | (40°C(104°F), 95%RH, 16hrs) 3 cycles | Passed |
| Durability against temperature | MIL-STD-202D-106(*1) 3 cycles Cross hatch tape peeling |
No peeling off No cracks |
| Weathering resistance | Sunshine Weather-O-Meter 500hrs | Passed |
| Solvent resistance | 100 rubs with 99% ethanol | No peeling off. Not resolved |
| 50 rubs with regular gasoline | No peeling off. Little resolved |
|
| Detergent resistance | 50 rubs with detergent | No peeling off No cracks |
| Oil resistance | 50 rubs with hand cream | No peeling off No cracks |
| Abrasion resistance | 100 rubs with eraser | No peeling off Slight scar |
(*1)MIL-STD-202D-106(standard by US army)
60-70°C(140-158°F) 6hrs ---> room temp. 4hrs ---> 60-70°C(140-158°F) 4hrs ---> room temp. 3hrs ---> -20+-5°C(-4+-9°F) 4hrs ---> room temp. 3hrs
- Value in this information is obtained in experiment and no guarantee is implied.
- Weathering resistance depends on the color. Please refer to lightfastness chart before use. Matched colors, especially smoke colors and pale colors, are inferior to standard colors in weathering resistance.
|
|
|
|
 |
 |
||